Abstract
The dry-wet cycle corrosion behavior of low alloy steel (Q355B) and 700 MPa grade Ni, Cr composite weathering steel (4 wt% Ni-5 wt% Cr) in 2 wt% NaCl solutions was studied. The distribution characteristics of elements and phases in the corrosion products after 360 h corrosion cycle were analyzed by SEM and Raman spectroscopy. The formation mechanism of protective rust layer of Ni, Cr composite weathering steel in simulated marine environment was briefly described. The results show that the corrosion products of Q355B appear obvious stratification, and the rust layer of Ni, Cr composite weathering steel has no longer stratified. The Ni, Cr composite weathering steel forms a cationic selective rust layer during the corrosion process, which effectively prevents the penetration of Cl- and exhibits excellent corrosion resistance, the corrosion rate of Ni, Cr composite weathering steel after 72 h-360 h corrosion cycle is 1/8–1/3 of that of Q355B. The value of α/γ * increases with the extension of corrosion cycle, which is reach to 1.0 after 360 h corrosion cycle. The corrosion potential increases with the extension of corrosion cycle, the corrosion current density fluctuates slightly around 100 × 10−6 A/cm2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.