Abstract
Low temperature plasma surface alloying with carbon (i.e. plasma carburising) of Stellite 21 Co–Cr alloy was conducted at temperatures from 400 to 500°C for 15 h in a gas mixture of 98 vol.-%H2 and 2 vol.-%CH4. The surface treated layers were characterised by XRD, SEM and microhardness tests. The corrosion and corrosive wear behaviour of the plasma carburised Stellite 21 Co–Cr alloy were studied respectively using electrochemical tests and well designed reciprocating wear tests in 3·5% NaCl solution. The results show that low temperature (≤460°C) plasma carburising can improve the corrosion resistance of Stellite 21 alloy; the corrosive wear resistance of Stellite 21 can be enhanced by up to three times; and the best corrosive wear resistance is achieved at the highest treating temperature (500°C). The detailed studies on the wear tracks indicate that the corrosive wear process was dependent on the individual wear and corrosion, as well as the synergetic effect.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.