Correlation of viscosity ratio, morphology, and mechanical properties of polyamide 12/natural rubber blends via reactive compatibilization

Abstract

Natural rubber (NR)-modified polyamide 12 (Nylon12/NR) was produced by melt blending Nylon12 and NR in the presence of polystyrene/maleated natural rubber (PS/MNR) copolymer as a reactive compatibilizer. The influence of compatibilizer loading on viscosity ratio, morphology, and mechanical properties of the blends was investigated. As a consequence of the reactive blend between Nylon12 and maleated NR in PS/MNR, the formation of amide and succinimide linkages was set at rubber-Nylon12 interfaces. Thus the dispersion of rubber particles was improved, and the particle coalescence was prevented so that the fine morphology with good interfacial adhesion was stabilized. This also resulted to enhance the blend viscosity and to lower viscosity ratio. The data revealed strong correlation between low viscosity ratio and fine spherical morphology of the compatibilized blends. An optimum PS/MNR compatibilizer content was at 7 phr to produce good dispersion of small rubber domains (size ≤0.3 μm) in Nylon12 matrix. Thermal properties by DSC revealed that crystallization temperature of Nylon12 was lowered by the presence of NR and crystallinity of Nylon12 was slightly affected by the PS/MNR content. An enhancement of mechanical properties, especially the impact energy was observed without suffering the tensile and flexural properties. Compared to the neat Nylon12, the compatibilized blends showed an increase in impact energy by a factor of 5. This large enhancement is successfully interpreted in term of the toughening effect by rubber phase of suitable dispersed size and the interparticle distance.