Abstract
The correlation of microstructure with the hardness and wear resistance of (TiC,SiC)/Ti-6Al-4V surface composites fabricated by high-energy electron-beam irradiation was investigated in this study. The mixtures of TiC, SiC, or TiC + SiC powders and CaF2 flux were placed on a Ti-6Al-4V substrate, and then an electron beam was irradiated on these mixtures using an electron-beam accelerator. The surface composite layers of 1.2 to 2.1 mm in thickness were formed without defects and contained a large amount (up to 66 vol pct) of precipitates such as TiC and Ti5Si3 in the martensitic matrix. This microstructural modification, including the formation of hard precipitates and a hardened matrix in the surface composite layer, improved the hardness and wear resistance. Particularly in the surface composite fabricated with TiC + SiC powders, the wear resistance was greatly enhanced to a level 25 times higher than that of the Ti alloy substrate, because 66 vol pct of TiC and Ti5Si3 was precipitated homogeneously in the hardened martensitic matrix. These findings suggested that high-energy electron-beam irradiation was useful for the development of Ti-based surface composites with improved hardness and wear properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.