Correlation of Microstructure and Texture in a Two-Phase High-Mn Twinning-Induced Plasticity Steel During Cold Rolling

Abstract

The evolution of microstructure and texture of a two-phase austenite-ferrite twinning-induced plasticity steel during cold rolling was investigated and different deformation mechanisms were found to become active with increasing thickness reductions. Optical microscopy showed the formation of brass-type shear bands across several austenite grains at reductions greater than 50 pct. TEM observations reveal the presence of deformation twinning in austenite. The austenite phase initially shows the Cu-type texture, i.e., Cu {1 1 2}〈1 1 1〉, Goss {0 1 1}〈1 0 0〉 with a spread toward Brass {1 1 0}〈1 1 2〉. With continued cold rolling, the Cu {1 1 2}〈1 1 1〉 component moves toward CuT component {552}〈115〉 and the other two components increase in intensity. There is also emergence of {111} fiber after 90 pct cold rolling. The ferrite phase exhibits the evolution of ND-rotated Cube component {001}〈110〉 along with 〈110〉 fiber at lower as well as at higher rolling reductions. An exception is at 75 pct reduction, when the ferrite texture contains {111} fiber in place of 〈110〉 fiber with a weak rotated-Cube component. Phase fraction analysis by X-ray diffraction indicates a decrease in the austenite fraction up to 75 pct reduction followed by an increase at 90 pct reduction. After 90 pct cold rolling, the phase fraction is similar to that of the “as-received” state. Elongated grains of ferrite phase in finer dimensions after 90 pct cold rolling indicate softening within that phase; at similar stage, there are finer scale austenite grains mostly at the grain boundaries. The above has been suggested to be related with the adiabatic heating during cold rolling due to the high strain hardening of the austenite phase.