Abstract

ABSTRACTA study correlating the leachability of 137 Cs from small-scale to large-scale cement forms was performed. The waste forms consisted of (a) organic ion exchange resins incorporated in Portland I cement, with a waste-to-cement ratio of 0.6 and a water-to-cement ratio of 0.4 (as free water) and (b) boric acid waste (12% solution) incorporated in Portland III cement, with a waste-to-cement ratio of 0.7. 137Cs was added to both waste types prior to solidification. The sample dimensions varied from 1 in. ×1 in. to 22 in. × 22 in. (diameter × height). Leach data extending over a period of 260 days were obtained using a modified IAEA leach test. A method based on semi-infinite plane source diffusion model was applied to interpret the leach data, which allows prediction of the amount of 137Cs leached from the forms as a function of leaching time and waste form dimensions. A reasonably good agreement between the experimental and calculated data was obtained for both types of cement waste forms.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.