Abstract
Electrospinning is an increasingly popular technique for obtaining scaffolds for skin regeneration. However, electrospun scaffolds may also have some disadvantages, as the densely packed fibers in the scaffold structure can limit the penetration of skin cells into the inner part of the material. Such a dense arrangement of fibers can cause the cells to treat the 3D material as 2D one, and thus cause them to accumulate only on the upper surface. In this study, bi-polymer scaffolds made of polylactide (PLA) and polyvinyl alcohol (PVA) electrospun in a sequential or a concurrent system were investigated in a different PLA:PVA ratio (2:1 and 1:1). The properties of six types of model materials were investigated and compared i.e.; the initial materials electrospun by the sequential (PLA/PVA, 2PLA/PVA) and the concurrent system (PLA||PVA) and the same materials with removed PVA fibers (PLA/rPVA, 2PLA/rPVA, PLA||rPVA). The fiber models were intended to increase the porosity and coherent structure parameters of the scaffolds. The applied treatment involving the removal of PVA nanofibers increased the size of interfibrous pores formed between the PLA fibers. Ultimately, the porosity of the PLA/PVA scaffolds increased from 78 % to 99 %, and the time of water absorption decreased from 516 to 2 s. The change in wettability was induced by a synergistic effect of decrease in roughness after washing out and the presence of residual PVA fibers. The chemical analysis carried out confirmed the presence of PVA residues on the PLA fibers (FTIR-ATR study). In vitro studies were performed on human keratinocytes (HaKaT) and macrophages (RAW264.7), for which penetration into the inner part of the PLAIIPVA scaffold was observed. The new proposed approach, which allows the removal of PVA fibers from the bicomponent material, allows to obtain a scaffold with increased porosity, and thus better permeability for cells and nutrients.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.