Abstract
Five different grain sizes are produced in 0.17wt% carbon steel using varying rates of cooling from austenitization temperatures. Controlled furnace cooling from 1100°C and 950°C produces coarse ferrite grains of 40µm and 32µm diameter, respectively, along with partial degeneration of cementite lamellae within pearlite regions. Execution of intermediate (oven at 300°C) and fast (air) cooling from 950°C develops finer polygonal ferrite (19µm and 14µm) with increased degeneration of pearlite; while repeated heating and force air cooling around 950°C produces a minimum ferrite grain size of 9µm and complete degeneration of the pearlite regions. Influence of micro-alloying is observed by precipitation of fine carbides in grain-refined structures. Tensile test results show improvement in strength values and ductility parameters with the progress of grain refinement. By comparing the improved yield strength values with the classic Hall–Petch relation: σ=σi+Kd−1/2, a deviation is observed in the exponent of grain size. Lüders strain becomes larger with decrease in ferrite grain size. The flow curves and strain hardening exponents as derived for different grain sizes show increasing plasticity with grain refinement. Rate of strain hardening also becomes higher with grain refined structures. Ferrite grain refinement results in a dominating inter-crystalline mode of tensile fracture.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.