Abstract
Hardness (H) may not be sufficed as a property the same way density (ρ) felt short as a measure of physical property, hence there is the need to correlate H with other property (ies). The porous nature of the material, dislocations and addition of constituents to the aluminium matrix affect the conductivity (Ծ) of alloys among other defects. In this article, attempt to fill the gap in recycling beverage can (RBC) for bumper beam applications was made by producing a 7xxx alloy from 3xxx alloy. About 80 % of the raw materials used in this alloy were sourced from secondary means. Stir casting route was adapted. Aluminium (Al) chips, 70 % Cu- 30 % Al, Manganese (Mn) and Magnesium (Mg) were charged in that order. The relationship between Ծ, H and ρ of the new alloy was established in the As-Cast (AC), annealed (O), natural aged (T4) and artificial aged (T6) conditions. In AC, an alloy of Al- 4.0 Zn-1.5Mg-0.35Cu-Mn recorded the peak obtainable Ծ and H of 3.7x107 m/S and 113.06 Hv with a ρ of 2.7464 g/ cm-3. The same alloy recorded peak Ծ and H in the O condition of 3.7x107 m/S and 102.6 Hv, whereas the ρ was 2.752 g/ cm-3. The T4 heat treatment (HT) deviated when the peak Ծ was 3.7x107 m/S, H and ρ were 58.94 Hv and 2.7551 g/ cm-3 respectively. T6 conditioned alloys delivered peak Ծ of 3.7x107 m/S in an alloy of Al- 4.0 Zn-1.5Mg-0.35Cu-Mn with a ρ of 2.7853 g/cm-3 and 60.26 Hv. HT and formation of precipitates were detrimental to Ծ and beneficial to H. Curve fittings were obtained and used in developing linear models for the relationship between H and Ծ within respective conditions unique to the experimental alloys.
Highlights
The roles of precipitate and dislocations in physical and mechanical properties of Al-Zn-Mg-Cu alloys were well known in the literature [1, 3]
Phases were formed from the addition of metallic alloying constituents. These additions were more detrimental to electrical Ծ in the solid solution conditions than in the T4 and T6 out of solution conditions, aluminium is known for high Ծ [1]
Aluminium was sourced from about 6 Kg Al-beverage cans collected from recycle hub at the University Tun Husain Onn Malaysia (UTHM) campus and collection Centre located in Parit Raja, Johor Malaysia
Summary
The roles of precipitate and dislocations in physical and mechanical properties of Al-Zn-Mg-Cu alloys were well known in the literature [1, 3]. Phases were formed from the addition of metallic alloying constituents. The relevance of the hardening phases formed by additional constituents is linked to H, ρ and other mechanical properties. Ծ predicts the phase transformation and the values may be indirect indication of the type, size and amount of precipitate formed [2]. This property is affected by the nature of precipitates [3]
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call