Abstract
In this work, the impact of oxygen vacancies and nitrogen-doped carbon coating on the sodium-ion storage properties of anatase TiO2 has been demonstrated. Oxygen vacancies and nitrogen-doped carbon coating were introduced simultaneously by the calcination of core-shell structured TiO2 spheres in a reducing atmosphere. Compared to the anatase TiO2 with and without oxygen vacancies, TiO2-x@NC exhibits much better electrochemical performance in the storage of sodium ions. A high reversible capacity of 245.6 mA h g-1 is maintained at 0.1 A g-1 after 200 cycles, and a high specific capacity of 155.6 mA h g-1 is achieved at a high rate of 5.0 A g-1. The significantly improved electrochemical performance of the core-shell structured anatase TiO2 spheres is attributed to the synergistic effect of the oxygen vacancies in the anatase lattice and surface nitrogen-doped carbon coating. This work provides an efficient strategy for improving the electrochemical performance of metal-oxide-based electrode materials for sodium-ion batteries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.