Abstract
Background:Polymerization shrinkage is an innate characteristic of thermo-polymerized denture base acrylic resin. Volumetric shrinkage is still a problem, although myriad material modifications. Ring-opening oxaspiro monomers have promising volumetric expansions of about 7%. These monomers have diminished the shrinkage in dental filling resins through copolymerization (CP). However, their CP with denture base resins is not reported yet.Purpose:The aim is to confirm the CP of an oxaspiro monomer with methyl methacrylate (MMA) by radical-cationic hybrid polymerization and to assess the degree of conversion (DC) of the formed copolymer.Materials and Methods:The oxaspiro monomer was synthesized by a transesterification reaction. The study groups were based on the composition and thermo-polymerization method. The control and E1 groups were thermo-polymerized in water-bath, whereas the E2 group in a laboratory autoclave. Both E1 and E2 groups contained the oxaspiro monomer and cationic initiator. E2 group had an additional radical initiator. The CP and DC were confirmed and assessed by infrared spectroscopy.Results:Accentuation of carbonyl peak, the disappearance of the spiro-carbon peak, and the appearance of ether linkages in experimental groups confirmed the ring-opening. E2 group had the highest DC.Conclusion:The oxaspiro monomer successfully copolymerized with MMA and had good DC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.