Abstract
The size of spherulites observed in the poly(butylene succinate-co-adipate) (PBSA) gel was found to be effectively controlled by the careful selection of the types of solvent and the gel preparation temperature. Additionally, the degradation behavior of the PBSA dried-gels with different sizes of spherulites was studied. By using different solvents, such as toluene (TOL), o-dichlorobenzene (o-DCB), and cyclohexanone (CHN), the diameter of the spherulites could be changed from 16.7 μm to 186.2 μm, while the gel preparation temperature was kept constant at 28 °C. The gel preparation temperature was then changed from −50 °C to 28 °C using CHN, and it was found that the diameter of the spherulites changed from 25.2 μm to 186.2 μm. Regarding the degradation behavior, the PBSA dried-gel with relatively smaller spherulites (∼20 μm in diameter) exhibited higher weight loss of over 80% at the immersion time of 6 days, while the PBSA dried-gels with relatively larger spherulites (∼186 μm in diameter) presented lower weight loss of below 30% at the immersion time of 6 days. It was therefore concluded that the degradation rate became lower with the increase in the size of spherulites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.