Abstract
Porous anodic tin oxide films with various pore diameters were synthesized by one-step anodization of Sn foil in 1M NaOH followed by 2h of annealing at 200°C. When the potential of 2V was applied during anodization, oxide layers with ultra-small nanochannels having diameter slightly above 10nm were obtained, and an average distance between neighboring pores was ∼20nm. On the contrary, applying the potential of 4V resulted in the formation of anodic films with much wider channels (∼40nm in diameter) and larger pore spacing (∼55nm). The composition of as formed samples was examined by XRD and XPS measurements. The as obtained anodic films were amorphous even after annealing. However, the greater Sn2+ ion content was observed for the sample anodized at 4V. In consequence, the porous oxide layer grown at the higher potential exhibited a red-shifted absorption edge as well as the lower optical band-gap in comparison to the sample synthesized at 2V. This fact was ascribed to a higher content of Sn2+ defects which are mainly responsible for a significant enhancement of photoelectrochemical activity of the material in the visible range. However, photoelectrochemical activity in the visible range was noticeable for anodic tin oxide films independently of the anodizing potential. We believe that such kind of self-supported electrodes can be promising candidates for photocatalytic and photoelectrochemical applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.