Controlled protein adsorption on PMOXA/PAA based coatings by thermally induced immobilization

Abstract

In this work, poly(2-methyl-2-oxazoline-random-glycidyl methacrylate) (PMOXA-r-GMA) and poly(acrylic acid)-block-poly(glycidyl methacrylate) (PAA-b-PGMA) copolymers were synthesized via cationic ring-opening polymerization (CROP) of 2-methyl-2-oxazoline (MOXA) and reversible addition-fragmentation chain transfer (RAFT) polymerization of acrylic acid (AA) followed by their random and block copolymerization with glycidyl methacrylate (GMA), respectively, and then characterized carefully. PMOXA/PAA based coatings were then prepared by simply spin coating the mixture of PMOXA-r-GMA and PAA-b-PGMA copolymer solutions onto silicon/glass substrates followed by annealing at 110 °C. The coatings were rigorously characterized by using X-ray photoelectron spectroscopy (XPS), the static water contact angle (WCA) test, ellipsometry and atomic force microscopy (AFM). The results demonstrated that the coating based mixed PMOXA/PAA brushes with desired surface composition could be attained by simply maintaining their percentage in the mixture of PMOXA-r-GMA and PAA-b-PGMA copolymer solutions. Finally, the switchable behavior of PMOXA/PAA based coatings toward bovine serum albumin (BSA) adsorption was investigated by fluorescein isothiocyanate-labelled BSA (FITC-BSA) assay and quartz crystal microbalance with dissipation monitoring (QCM-D), which indicated that the coating based mixed PMOXA/PAA brushes could control BSA adsorption/desorption from very low to high amount (>90% desorption) through adjusting the composition of PMOXA-r-GMA and PAA-b-PGMA solution used in preparing PMOXA/PAA based coatings upon pH and ionic strength change. Furthermore, PMOXA/PAA based coatings displayed efficient repeatability of reversible BSA adsorption/desorption cycles.