Abstract
With an eye toward using surface morphology to enhance heterogeneous catalysis, Pt nanoparticles are grown by atomic layer deposition (ALD) on the surfaces of SrTiO(3) nanocubes. The size, dispersion, and chemical state of the Pt nanoparticles are controlled by the number of ALD growth cycles. The SrTiO(3) nanocubes average 60 nm on a side with {001} faces. The Pt loading increases linearly with Pt ALD cycles to a value of 1.1 x 10(-6) g cm(-2) after five cycles. Scanning electron microscopy images reveal discrete, well-dispersed Pt nanoparticles. Small- and wide-angle X-ray scattering show that the Pt nanoparticle spacing and size increase as the number of ALD cycles increases. X-ray absorption spectroscopy shows a progression from platinum(II) oxide to metallic platinum and a decrease in Pt--O bonding with an increase in Pt--Pt bonding as the number of ALD cycles increases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.