Abstract
Many applications in nanotechnology require short and unentangled single-walled carbon nanotubes (SWCNT). Liquid-phase oxidative cutting gives nonuniform short tubes and causes significant material loss. Mechanical cutting is good for shortening SWCNT, but it leaves collapsed tube ends and might not be favorable for further manipulation. Solid-state reaction cutting is better for multi-walled carbon nanotubes than for SWCNT. Herein, we present a method combining mechanical and oxidative cutting. The SWCNT sample was first ground with a Wig-L-Bug grinding mill for 30min, introducing structural defects into the side walls of SWCNT. The treated SWCNT were then soaked in a Piranha solution, in which the oxidants attack the existing side wall defects and give a complete cut. According to statistical analysis from transmission electron microscopy, most of the shortened SWCNT fall in the range of 50–200nm. The material loss is 12.2wt%. The functional groups on the tube surface introduced by shortening were removed by refluxing in a soda lime/water suspension. Then, the carbon nanotubes were further annealed by sonicating in ethanol. After annealing, the defect level of shortened carbon nanotubes was reduced significantly, as determined by Raman spectroscopy, Fourier transform infrared spectroscopy and thermogravimetric analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have