Abstract
Fabricating porous polymer films with precise morphological control via a conventional phase separation method is challenging. Herein, porous polyimide (PPI) film formation kinetics was thoroughly investigated to understand the underlying phenomena during the thermally induced phase separation. The porous films were prepared using a poly(amic acid) (PAA) solution with a small-molecular phase dispersion agent (i.e., porogen), dibutyl phthalate (DBP), which is miscible with the PAA chains. Using amine-functionalized polyhedral oligomeric silsesquioxane (NH2-POSS) as an additional nucleating agent, sponge-like NH2-POSS end-capped PPI (PPI/NH2-POSSx) films were fabricated with tunable pore size (16.3–76.9 μm) and porosity (42.6–69.4 %). This ensured control over the porous structure of the PPI/NH2-POSSx film, providing desirable low dielectric properties (a minimum of 2 at 1 MHz) in broad frequency and temperature range as well as high thermal stability (Tg = 363–385 °C, T5% = 519–559 °C), and good mechanical strength (17–23 MPa). It was found that the porous structure and physical properties of the PPI/NH2-POSSx films can be readily engineered by tailoring the initial content of a removable porogen and cage silsesquioxane. This work will provide a new perspective on fabricating temperature-resistant low-dielectric porous polymer films with tunable pore sizes via thermal-driven spontaneous phase separation with efficient processability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.