Abstract
Epitaxial Ni films with various thicknesses were grown on (001)-oriented 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 (PMN–PT) substrates. Electric field tuning (E-tuning) of ferromagnetic resonance field (Hr) was utilized to investigate the magnetic response of Ni films along different film directions. Butterfly-like Hr vs E curves are shown when magnetic field is applied along film edge. While the combination of both loop-like and butterfly-like Hr vs E curves are observed for Ni film with thicknesses of 180 nm and 240 nm, and merely loop-like curves can be seen for film thicknesses of 330 nm and 510 nm, as magnetic field is applied along film diagonal. These interesting phenomena are assumed to be related to ferroelectric and ferroelastic domain switching in PMN-PT, film strain status, as well as magnetic anisotropy in Ni film. This work demonstrates the feasibility of control of anisotropic magnetic response via electric field in multiferroic heterostructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.