Control of ferroelectric phase transition in nano particulate NBT–BT based ceramics

Abstract

Abstract Lead free relaxor NBT–BT based ceramic compositions were prepared using sol–gel method. The samples were sintered around 1140 °C for 3–4 h in the air. The characterization was done using X-ray diffraction (XRD), filed emission scanning electron microscope (FESEM), energy dispersive spectrometry (EDS), Raman, Fourier transform infrared (FTIR), dielectric and P – E loop measurements. The XRD patterns recorded at room temperature confirmed the phase formation of the samples. From FESEM micrographs, the particle sizes were estimated for calcined powders and are found to be in the range of 50–70 nm. The analysis of both Raman and FTIR spectral data of the samples also indicated the distortion of NBT lattice with the addition of Ba 2+ and Nd 3+ ions. It was found that the dielectric and piezoelectric properties of NBT–BT compositions beyond the morphotrophic phase boundary (MPB) are rather sensitive to the presence of tetragonal phase in addition to the rhombohedral phase. NBT ceramics exhibit a decrease in diffusive factor with increasing BT content, implying a degradation of relaxor feature leading to the normal ferroelectric nature. The ceramic samples employed in the present study exhibited variation in P – E hysteresis loops.