Control of artificial pinning centers in REBCO coated conductors derived from the trifluoroacetate metal-organic deposition process

Abstract

The metal-organic deposition (MOD) process using metal trifluoroacetate salts (TFA) has the advantages of low-cost and high-scalability for the fabrication of REBa2Cu3Oy (REBCO, RE: rare earth elements) superconducting coated conductors (CCs) with high critical current density, in principle, because of its non-vacuum process. For the magnetic applications of CCs such as motors, magnetic resonance imaging and superconducting magnetic energy storage, further improvement of superconducting performance under magnetic fields is required. However, the in-field superconducting performance of REBCO CCs derived from the TFA-MOD process had been inferior to those derived from the vapor-phase process. In order to improve the in-field performance, the size control of the artificial pinning centers has been known as an effective way. In the early stage, the BaZrO3 (BZO) material, which was one of the effective materials in the CCs by the vapor-phase process, was also introduced in the TFA-MOD-derived CCs. The unique feature of the BZO material in the TFA-MOD process is the shape. The BZO in the TFA-MOD process formed the particle shape, although in the vapor-phase process it has a rod shape with a long axis elongating along the thickness direction. In addition, a special heat treatment for refining the BZO particles was developed, which is called the ‘interim heat treatment’. This heating profile made the in-field characteristics higher, although they were still lower than those of the vapor-phase process. Then, the new MOD process including ‘ultra-thin once coating’ was recently developed for further refinement of the BZO particles. The characteristics of the new TFA-MOD-derived CCs in magnetic fields have become compatible with those of the CCs derived from the vapor-phase process.