Abstract
An opposite interfacial exciton dissociation behavior at the metal (Al)/organic cathode interface in regular and inverted organic solar cells (OSCs) was analyzed using transient photocurrent measurements. It is found that Al/organic contact in regular OSCs, made with the blend layer of poly[[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b′]dithiophene-2,6-diyl]-[3-fluoro-2-[(2-ethylhexyl)carbonyl]thieno[3,4-b]-thiophenediyl]] (PTB7):3′H-Cyclopropa [8,25][5,6] fullerene-C70-D5h(6)-3′-butanoicacid,3′-phenyl-,methyl ester (PC70BM), always hampers the electron collection. However, this is not observed in their reverse geometry OSCs fabricated using the same PTB7:PC70BM blend system. The detrimental interfacial exciton dissociation in regular OSCs originates the compensation of field drifted photo-generated electrons at Al/organic interface. The unfavorable interfacial exciton dissociation can be eliminated, e.g., by interposing a ZnO-based interlayer between Al and organic layer, attaining an efficient electron collection, thereby power conversion efficiency.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.