Continuous ultrasonic devulcanization of carbon black-filled NR vulcanizates

Abstract

The continuous ultrasonic devulcanization of natural rubber (NR) filled with various concentrations of carbon black (CB) indicated a minimum of crosslink density and gel fraction at an intermediate amplitude, which is independent of CB content. An attempt was made to improve the efficiency of devulcanization by use of various chemicals (1,3 Diphenylguanidine, 2-Mercaptobenzothiazole, Thianaphthene). However, these experiments did not indicate any improvement in comparison with devulcanization without chemicals. An idea of adding fresh CB into devulcanized compound, which has been shown to improve mechanical properties in the case of styrene–butadiene rubber (SBR), was tested in the present study for CB filled NR compound. The obtained result indicated that an addition of fresh CB to devulcanized CB-filled NR did not lead to an improvement in mechanical properties upon revulcanization. The revulcanization recipe was optimized to improve the mechanical properties of revulcanized CB-filled NR vulcanizates. It was found that CB-filled NR upon revulcanization retained its strain-induced cystallizability with the tensile strength and elongation at break at about 50 and 70% level of the virgin vulcanizates. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 79: 2340–2348, 2001