Continuous and discontinuous fatigue crack growth of irradiated ultrahigh molecular mass polyethylene in saline solution at 37�C

Abstract

To provide data for prosthesis design, the fatigue crack growth resistance of irradiated ultrahigh molecular mass polyethylene (UHMMPE) in saline solution at 37°C was determined from tests performed on compact tension specimens, comparable in size to the components in knee prostheses. The specimens were cyclically loaded by using a sinusoidal wave form at 1 Hz with a minimum-to-maximum load ratio of 0.1. Scanning electron microscopic fractography was used to examine the fracture surfaces. At higher stress levels, the Paris's Law was used to analyse the data, and a striation pattern with each striation corresponding to multi-cycles was observed. At lower stress levels, discontinuous fatigue crack growth was found, a phenomenon which dominated the fatigue life of the material and had not been reported previously in this material. A craze zone ahead of the crack tip was observed, which formed the discontinuous crack growth band with a length relevant to the Dugdale plastic zone length.