Containerless solidification of undercooled oxide and metallic eutectic melts

Abstract

Abstract A high-speed video was employed to monitor the in situ recalescence of undercooled oxide Al2O3–36.8 at.% ZrO2 and metallic Ni–18.7 at.% Sn eutectics that were processed on an aero-acoustic levitator and an electromagnetic levitator, respectively. For the oxide eutectic, the entire sample becomes brighter and brighter without any clear recalescence front during spontaneous crystallization. When the sample was seeded at desired undercoolings, crystallization started from the seeding point and then spread through the entire sample. Microstructures of the oxide solidified via both the spontaneous crystallization and external seeding consist of many independent eutectic colonies at the sample surface, indicating that copious nucleation takes place regardless of melt undercooling and solidification mode. For the metallic eutectics, two kinds of recalescence are visualized. The surface and cross sectional microstructures reveal that copious nucleation is also responsible for the formation of independent eutectic colonies distributing within the entire sample. It is not possible to measure the growth velocity of a single eutectic colony using optical techniques under the usual magnification. The conventional nucleation concept derived from single-phase alloys may not be applicable to the free solidification of the undercooled double-phase oxide and metallic eutectic systems.