Abstract
Oriented poly(vinyl alcohol) (PVA)/graphene oxide (GO) nanocomposite hydrogels with different draw ratios were prepared by stretching during a freezing/thawing process. The PVA/GO samples with a draw ratio of 200% had significantly enhanced mechanical properties by formation of a microfibrillar structure, while the tensile strength and compressive modulus respectively reached as high as 11.60 and 4.05 MPa, outperforming the unoriented samples with an increase of 167% and 540%, respectively. During the freezing/thawing process under stress, the orientation factor, crystallinity, and cross-linking density (υe) of PVA/GO samples increased steadily, while the regularly arranged fibrillar bundle structure increasingly formed, and the size of the porous structure decreased. Besides that, additional PVA crystals formed with decreasing long period (L), crystalline region (Lc), and lamellae size (Llateral). Due to the synergic orientation of GO sheets and nucleation effect, the oriented PVA/GO samples showed an or...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.