Abstract
Pure hydroxyapatite (HA) has attracted much attention in the field of bone repair materials due to its strong potential for bioavailability, but its low osteogenic activity and non-bacterial inhibition limits its further application in this field. Therefore, in this study, strontium (Sr)-doped hydroxyapatite (HA-Sr) microspheres with a high specific surface area were prepared without adding a templating agent. On this basis, berberine hydrochloride (BBH), a Traditional Chinese antimicrobial agent with excellent antibacterial ability, was loaded to overcome traditional limitations and construct a material with good osteogenic activity and antibacterial capacity. A series of characterization results showed the doping of Sr did not affect the physical phase and morphology of HA but altered its chemical composition and crystallinity, and HA-Sr microspheres had good microscopic morphology and ion retardation, which laid the foundation for the subsequent improvement of the integrated capacity. In vitro cell experiments showed that Sr ions could significantly promote the differentiation of rBMSCs at a range of doping concentrations. In this study, the optimal doping concentration of 3% was systematically screened by cell proliferation assay, alkaline phosphatase staining and alizarin red staining in a small concentration range (1–7%). Subsequently, BBH was loaded with 3% Sr ion-doped HA microspheres to construct the drug loading model. And the sustained release test and antibacterial test further proved that its antibacterial performance was enhanced. The combined results of these experiments indicated that this material was successfully constructed with good osteogenic activity and antibacterial property, and its biological property was greatly improved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.