Abstract
High temperature compressive deformation behaviors of as-cast Ti-43Al-4Nb-1.4W-0.6B alloy was investigated at temperatures ranging from 1323 K to 1473 K, and strain rates from 0.001 s−1 to 1 s−1. The results indicated that the true stress—true strain curves show a dynamic flow softening behavior. The flow curves after the friction and the temperature compensations were employed to develop constitutive equations. The effects of temperature and the strain rate on the deformation behavior were represented by Zener-Holloman exponential equation. The influence of strain was incorporated in the constitutive analysis by considering the effect of the strain on material constants by a five-order polynomial. A revised model was proposed to describe the relationships among the flow stress, strain rate and temperature and the predicted flow stress curves were in good agreement with experimental results. Appropriate deformation processing parameters were suggested based on the processing map which was constructed from friction and temperature corrected flow curves, determined as 1343 K, 0.02 s−1 and were successfully applied in the canned forging of billets to simulate industrial work condition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.