Abstract The deformation behavior and microstructural evolution of as-cast 254SMO super-austenitic stainless steel (SASS) were studied by hot compressive tests in the temperature range 900–1200 °C, and in the strain rate range 0.01–10 s −1 . The results show that the single peak characteristic appears on almost all the obtained flow curves, indicating that DRX is the primary softening mechanism. Either increasing deformation temperature or decreasing strain rate makes the flow stress level reduce remarkably. The hot deformation activation energy and the stress exponent are calculated to be 577.845 kJ/mol and 4.62 by the regression analysis of sine hyperbolic function, respectively. From the deformed microstructures, it is found that the DRX nucleates mainly through grain boundary bulging but occasional through subgrain evolution only occurred at high strain rates and high temperatures. The critical stress and corresponding strain for DRX can be expressed through the dimensionless parameter, Z / A . The critical ratios of σ c / σ p and e c / e p are also identified, which are 0.98 and 0.72, respectively. Moreover, the DRX kinetics for as-cast 254SMO SASS can be represented in the form of Avrami equation, and the predicted volume fraction of new grains based on the developed model agrees well with the experimental results.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.