Abstract
Dynamic tensile moduli of polyethylene--nickel-coated carbon fiber (NiCF) composites with 10 and 4 vol % NiCF contents under electrical field were measured by a homemade instrument in the frequency range of 100--0.01 Hz. The drastic descent of the storage modulus of the composite with 10 vol % was verified in lower frequency range with elevating surface temperature (T(s)) by self-heating (Joule heat). The composite was cut when T(s) was beyond 108 °C. On the other hand, the measurement of the composite with 4 vol % beyond 88 °C was impossible, since T(s) did not elevate because of the disruption of current networks. Incidentally, the dynamic tensile moduli by external heating could be measured up to 130 and 115 °C for 10 and 4 vol %, respectively, but the two composites could be elongated beyond the above temperatures. Such different properties were analyzed in terms of crystal dispersions, electrical treeing, and thermal fluctuation-induced tunneling effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.