Abstract
The miscibility of the mixed monolayer behavior of different polystyrene-poly(methyl methacrylate) (PS-b-PMMA; PS-co-PMMA; PS-r-PMMA) with phenoxy resin(Phr) was studied from the measurements of surface pressure-area per molecule (π-A) isotherms using the Wilhelmy plate method with a KSV model mini-trough at three different temperatures (10˚C, 25˚C and 40˚C). The miscibility and non-ideality of the mixed monolayers were examined by calculating the excess surface area as a function of composition. The analysis of surface pressure-area per molecule (π-A) isotherms and excess area showed that mixed monolayers exhibit intermolecular interaction. When the pressure increases, the deviation can change from positive to negative. The mixed PS-b-PMMA monolayers exhibited mostly negative excess area among three studied PS-PMMA. The results of the mixed PS-co-PMMA monolayers were similar to those of mixed PS-r-PMMA likely because of close chain arrangements. Phr was found to be in the majority miscible with PS-PMMA at the air/water interface likely because of hydrogen bonding between Phr and PS-PMMA and confinement inducement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.