Abstract
We report on the conductivity and adhesion enhancement of indium tin oxide (In 2O 3:Sn; ITO) nanoparticle films by the application of polymers as matrix material. We fabricated ITO layers at a maximum process temperature of 130 °C by modifying and spin-coating nanoparticulate ITO dispersions. Dispersions containing the organic film-forming agent polyvinylpyrrolidone (PVP) and the organofunctional coupling agent 3-methacryloxypropyltrimethoxysilane (MPTS) have been developed to obtain transparent and conducting coatings on substrates which do not withstand high process temperatures like polymers or already processed glasses. The layers were cured by UV-irradiation as well as by low-temperature heat treatment ( T = 130 °C) in air and under forming gas atmosphere (N 2/H 2). The influence of the additives on the electrical, optical, morphological and mechanical layer properties is reported. Compared to best pure ITO layers (3.1 Ω − 1 cm − 1 ), the ITO–MPTS–PVP nanocomposite coatings exhibit a conductance of 9.8 Ω − 1 cm − 1 . Stable sheet resistances of 750 Ω/□ at a coexistent transmittance of 86% at 550 nm for a layer thickness of about 1.3 µm were achieved. The conductance enhancement is a consequence of the consolidation of the ITO nanoparticle network due to the acting shrinkage forces caused either by drying in the case of PVP or UV-irradiation induced condensation and polymerization reactions in the case of MPTS.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.