Abstract
The study described sought further understanding of the synergies in a mix of CDW pozzolans, containing (calcareous and siliceous) concrete and glass waste, used to prepare ternary eco-cement paste bearing 7% of the binary blend at concrete/glass ratios of 2:1 and 1:2. The mineralogical phases in the 2-day, 28-day, and 90-day cement matrices were identified and monitored using XRF, XRD-Rietveld, SEM-EDX, FT-IR, and NMR. The findings showed that changes in the reaction kinetics in the ternary blended pastes relative to OPC pastes depended on the nature of the recycled concrete and the glass content. Adding the binary mix bearing calcareous concrete (at a ratio of 2:1) favoured ettringite, portlandite, and amorphous phase formation, whilst the blends with siliceous concrete favoured C-S-H gel formation. Monocarboaluminate was detected in the 90-day siliceous concrete and glass pastes in amounts similar to those found in the reference OPC paste.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.