Abstract
AbstractIn this paper, the kinetics of TiN, V(C,N)) and AlN precipitation in microalloyed steel during continuous casting is investigated experimentally and theoretically. The precipitate phase fraction, mean radius, number density and composition are simulated with the thermo‐kinetic software MatCalc and compared with experimental results obtained from transmission electron microscopy analysis. A new methodology for modelling precipitation in cast steel is proposed, which consists of two parts: First, a Scheil – Gulliver simulation, which is carried out to obtain information on the amount of microsegregation during solidification. Then, based on this information, two precipitation kinetics simulations are performed: One with the chemical composition representative for the solute‐poor core of the secondary dendrite arms, the other with the composition of the residual liquid at a fraction of 5%, corresponding to the segregated solute‐rich interdendritic regions. The results of the computer simulations using the new methodology are in good agreement with experimental observation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.