Abstract
Composite alkali activated cements of waste glass (WG) and ground granulated blast furnace slag (GGBFS) were studied in pastes for 720 daysThe factors for the experimental design (Taguchi method) were: %WG, sodium silicate modulus (Ms), curing temperature, and %ultra-fine WG; the response variable was the compressive strength. 29Si Nuclear Magnetic Resonance, scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction indicated that the reaction products in pastes with WG contents greater than 50% were predominantly silica gel, which reached up to 140 MPa; on the other hand, phases of C-S-H/C-A-S-H predominated in pastes with GGBFS content > 50%, which showed high early strength. Silica gel performed as a cementitious phase contributing to the 720-days strength, but it was unstable underwater; however, it was stabilized when intermixed with C-S-H/C-A-S-H. Curing at 40-60 °C promoted cracking and strength loss after 14 days.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.