Abstract
Ir-base alloys with the fcc and L12-Ir3X (X = Nb, Zr) two-phase structure have been developed as next-generation high-temperature materials. The compressive creep behavior of Ir-Nb and Ir-Zr alloys was investigated at 2073 K under 137 MPa. The effect of addition of the third element, Zr, on the creep behavior of an Ir-Nb alloy was also investigated at 2073 K for 137 MPa. The creep rate became two orders lower by addition of a small amount of Zr. The lattice misfit change between the fcc and L12 two phase by addition of Zr and the deformation structure in binary and ternary alloys after a creep test were also investigated. The creep behavior is discussed in terms of the lattice misfit, precipitate shape, and their distribution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.