Abstract
C/SiC composite sandwich structure with stitched lattice core was fabricated by a technique that involved polymer impregnation and interweaving. The mechanical behaviors of C/SiC composite sandwich structure were investigated at room temperature. The out-of-plane compressive strength was 20.97MPa while modulus was 1473.55MPa. The microstructural evolution on compression fracture surfaces of the stitching yarns was investigated by scanning electron microscopy, and the damage pattern of fibers on compression fracture surface was presented and discussed. Under an in-plane compression loading, the C/SiC composite sandwich structure displayed a linear-elastic behavior until failure. The peak strength and average modulus are 165.61MPa and 19.74GPa, respectively. The failure of the specimen was dominated by the fracture of the facesheet.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.