Abstract
The development of creep-resistant magnesium alloys that avoid the use of rare-earth alloying elements is an important area of research. The creep response of Mg–Al–Ca alloy containing barium (DieMag422) was compared to that of commercially available creep resistant magnesium alloys AE42 and MRI230D. The creep tests were performed between 175°C and 240°C at stresses between 60MPa and 120MPa. From the temperature and stress dependence of the minimum creep rate, the apparent activation energy Qc and the stress exponent n for creep were calculated. The concept of a threshold stress was applied. True stress exponents nt close to 5 were calculated. Microstructural investigations and phase analysis were performed on the as-cast materials as well as after creep. Fine precipitates could be identified that justified application of the concept of threshold stress. The DieMag422 alloy shows an improvement in creep resistance at low stresses compared with the other two alloys AE42 and MRI230D.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.