Compression and Fatigue Testing of High-Strength Thin Metal Sheets by Using an Anti-Buckling Device

Abstract

BackgroundThe modelling of the sheet metal forming operations requires accurate and precise data of the material plastic behaviour along non-proportional strain paths. However, the buckling phenomenon severely limits the compressive strain range that could be used to deform thin metal sheets.ObjectiveThe main aim of this paper was to propose an effective device, that enables to determine of accurate stress-strain characteristics of thin metal sheet specimens subjected to axial deformation without buckling and with a special emphasis on friction correction.MethodsIn this paper, an anti-buckling fixture was proposed to assess the deformation characteristics of X10CrMoVNb9-1 (P91) power engineering steel, and DP500 and DP980 dual-phase steels, under compression loading. The fixture enables monitoring of the friction between the specimen and supporting blocks during the test, and thus the precise stress response of the material could be determined.ResultsThe effectiveness of the fixture was evaluated under tension–compression cyclic loading and during the compression tests in which high-strength thin metal sheets were successfully deformed up to 10% without specimen buckling. Furthermore, the successful determination of a friction force variation between supporting blocks and the specimen during tests enabled to determine an actual force acting on the specimen.ConclusionsThe proposed testing fixture was successfully assessed during the compression and cyclic tension–compression of high-strength thin metal sheets as no buckling was observed. Its advantage lies in adapting to change its length with specimen elongation or shrinkage during a test. The friction force generated from a movement of both parts of the device could be effectively monitored by the special strain gauge system during testing and thus its impact on the stress-strain characteristics could be successfully eliminated.