Pulse electrodeposition of Cu-Zn compositional modulated multilayer alloy (CMA) coatings was carried out onto AISI 304 stainless steel substrate using an environmentally friendly alkaline non-cyanide electrolytic bath. Cu-Zn alloy multilayer coating was co-electrodeposited using a trapezoidal pulse current. Multilayer coatings can have two different metals in layers or two-phase mixtures. Different sets of multilayers of 10, 20, 50, and 100 were done using a trapezoidal pulse current. In the trapezoidal pulse current module, during the higher current stage (0.1 A) Zn was deposited as compared to the lower current module (0.02 A) where Cu was deposited. Microstructural and structural analysis of the coatings confirmed nanocrystalline morphology with peaks corresponding to crystallographic planes of (002), (111), (020), and (022). Deposited coatings are hydrophilic in nature. The microhardness of the coatings is decreased with an increase in the number of layers deposited.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.