Compositional segregation and electrical properties characterization of [001]- and [011]-oriented co-growth Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystal

Abstract

A Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 relaxor ferroelectric single crystal boule of 3 in. diameter was grown using [001]- and [011]-oriented co-growth crystals as seeds by the modified Bridgman method. The as-grown crystal boule was divided into two growth regions [001] and [011]. The composition and the electrical properties of samples of the two regions were characterized in detail along the growth direction in the whole crystal boule. The PT content of [001]-grown samples increased from 27.7 to 36.8 mol. % along the growth direction, especially they are averagely higher about 0.7 mol. % than those of [011]-grown samples at the same growth position. The PMN content of [001]-grown samples decreased from 43.0 to 34.8 mol. %, which is lower than that of the corresponding [011]-grown samples. The compositional segregation behavior along [001] and [011] growth directions was discussed based on the crystal growth theories. Variations in the rhombohedral to tetragonal phase transition temperature (TRT), the piezoelectric properties, the coercive electric field and the remnant polarization of [001] samples were discussed according to changes in compositional segregation and crystal anisotropy. Under the exact same growth conditions, the [011]-grown crystal has a larger composition segregation effect than that of the [001]-grown crystal. This result provides a positive effect on analysing the nature and reducing the effect of compositional segregation.