Abstract
Cu/In bi-metal stacked structures were prepared on Mo coated soda lime glass substrates using electrodeposition method. These metallic precursors were selenized at 550 °C for 60 min to synthesize the CuInSe2 (CIS) thin films in a thermal evaporator chamber with an Se overpressure atmosphere. The composition ratios of CIS thin films were systematically controlled using the coulometric method of the electrodeposition, where the accumulated coulomb of In layers was varied from 1062 to 6375 mC/cm2. As a result, the stoichiometric CIS film was obtained in the Cu/In coulomb ratio of 0.6. Highly crystallized CIS films were produced from the liquid Cu-Se phase in the Cu/In coulomb ratio of ≥0.6. In contrast, the crystallinity and grain size were degraded in the In-rich region. We found that the Cu/In composition ratio of CIS films was linearly proportional to the precursor thickness determined by the coulomb ratio.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.