Abstract

Alloys of Tb0.2Dy0.8−xPrx(Fe0.8Co0.2)1.93 (0 ≤ x ≤ 0.40) are arc melted and investigated for structural, magnetic and magnetoelastic properties by means of X-ray diffraction (XRD), a vibrating sample magnetometer and a standard strain technique. The 20 at.% Co substitution for Fe is shown to enable the formation of the single Laves phase with a high Pr content up to x = 0.25. Experimental evidence for magnetocrystalline-anisotropy compensation between Pr3+ and Dy3+ ions is obtained in the Laves phase system. The easy magnetization direction (EMD) at room temperature rotates from <100> to <110> axis when x increases from 0 to 0.40. The linear anisotropic magnetostriction λa (=λ||–λ⊥) increases with increasing Pr content when x ≤ 0.25 ascribed to both the larger magnetostriction of PrFe2 than that of DyFe2 and the decrease of the resulted anisotropy due to compensation. The composition anisotropy compensation is found to be around x = 0.25, shifting to the Pr-rich side at room temperature as compared to the Co-free counterpart Tb0.2Dy0.8−xPrxFe1.93 system. The Tb0.2Dy0.55Pr0.25(Fe0.8Co0.2)1.93 alloy has good magnetoelastic properties at room temperature, that is, a low anisotropy and a high low-field magnetostriction λa ∼140 ppm at 1 kOe.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.