Abstract
The (1 1 1)A and (1 1 1)B surfaces of GaAs chemically treated in HCl-isopropanol solution (HCl-iPA) and annealed in vacuum were studied by means of X-ray photoelectron spectroscopy (XPS), low-energy electron diffraction (LEED) and electron energy loss spectroscopy (EELS). To avoid uncontrolled contamination, chemical treatment and sample transfer into UHV were performed under pure nitrogen atmosphere. The HCl-iPA treatment removes gallium and arsenic oxides, with about 0.5–3 ML of elemental arsenic being left on the surface, depending on the crystallographic orientation. With the increase of the annealing temperature, a sequence of reconstructions were identified by LEED: (1 × 1) and (2 × 2) on the (1 1 1)A surface and (1 × 1), (2 × 2), (1 × 1), (3 × 3), (√19 × √19) on the (1 1 1)B surface. These sequences of reconstructions correspond to the decrease of surface As concentration. The structural properties of chemically prepared GaAs(1 1 1) surfaces were found to be similar to those obtained by decapping of As-capped epitaxial layers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.