Abstract
Compositions of deposits forming on engines parts operated with landfill gas (LFG) were analyzed. The deposit compositions were compared before and after the installation of activated carbon system for treatment of LFG. Deposits forming on the spark plugs had significantly higher levels of calcium, chromium, and nickel in comparison to those forming on the engine heads. The LFG contained about 9.5 ± 0.4 mg/m3 total siloxanes, majority of which were octamethylcyclotetrasiloxane (D4) (5.0 ± 0.2 mg/m3), decamethylcyclopentasiloxane (D5) (2.9 ± 0.1 mg/m3) and hexamethyldisiloxane (L2) (1.6 ± 0.1 mg/m3). The samples collected from the engine heads before the activated carbon treatment of LFG had significantly high levels of silicon (149,400 ± 89,900 mg/kg) as well as calcium (70,840 ± 17,750 mg/kg), sulfur (42,500 ± 11,500 mg/kg), and zinc (22,300 ± 7200 mg/kg). After the activated carbon treatment, silicon levels decreased significantly; however, deposits had higher sulfur content (104,560 ± 68,100 mg/kg) indicating that the activated carbon released some sulfur during treatment. The analyses indicate that zinc and calcium originated from the additives in the lube oil while lead, aluminum, copper, nickel, iron, chromium were due to the engine wear.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.