Abstract

Constituent and dispersoid phases in two Direct Chill-cast 3xxx aluminum alloys after low-temperature annealing, with different silicon content have been studied. The lattice parameters, chemical composition, morphology and orientations relationships of constituent particles with regard to Al matrix have been addressed. Al(Fe,Mn) is found to be the most prominent constituent phase in the alloy with a low Si content. The orientation relationship between aluminum matrix and this phase is determined as , , which is consistent with the orientation relationships of Al(Fe,Mn) dispersoids. –Al(Fe,Mn)Si constituent particles in the Si rich alloy have been found to have various possible orientations. A gradient of Fe content is found in the –Al(Fe,Mn)Si dispersoids due to slow diffusion of Fe into dispersoids during annealing.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.