Abstract
Hardened C3S paste cured for 1 year at 20°C was examined to confirm the composition and the morphology of hydrated tricalcium silicate. A new technique was used in which the samples for scanning electron microscopy (SEM) and electron probe microanalysis (EPMA) were etched in 1% HNO3‐alcohol or in glycerol‐alcohol (4:6 by volume). After the surface was etched in 1% HNO3‐alcohol, SEM clearly showed the difference in texture in the outer and inner C‐S‐H products. The existence of a zonal texture within the inner C‐S‐H products was shown, in addition to the unreacted core; particles 0.1 to 0.2 μm in diameter were observed. After free CH extraction with glycerol‐alcohol, two new types of C‐S‐H grains could be identified. One type has a smooth surface, which seems to be produced from C3S grains trapped within the growing CH crystals in the early stage of hydration, the C/S mol ratio for these being >3. The other type is covered with many acicular outer C‐S‐H gel hydration products and has a C/S mol ratio >3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.