Composition and microstructure of zirconium and hafnium germanates obtained by different chemical routes

Abstract

The phase composition and morphology of zirconium and hafnium germanates synthesized by ceramic and co-precipitation routes were studied. The products were characterized using high-temperature X-ray diffraction analysis (XRD), Raman spectroscopy, scanning electron microscopy (SEM) and thermal (TG/DTA) analysis. To investigate the phase composition and stoichiometry of compounds the unit cell parameters were refined by full-profile Rietveld XRD analysis. The morphology of products and its evolution during high-temperature treatment was examined by SEM analysis.It was stated that there is the strong dependence of the phase composition and morphology of products on the preparation route. The ceramic route requires a multi-stage high-temperature treatment to obtain zirconium and hafnium germanates of 95% purity or more. Also, there are strong diffusion limitations to obtain hafnium germanate Hf3GeO8 by ceramic route. On the contrary, the co-precipitation route leads to the formation of nanocrystalline single phase germanates of stoichiometric composition at a relatively low temperatures (less than 1000°C). The results of quantitative XRD analysis showed the hafnium germanates are stoichiometric compounds in contrast to zirconium germanates that form a set of solid solutions. This distinction may be related to the difference in the ion radii of Zr and Hf.