Composition and annealing effects on superconductivity in sintered and arc-melted Fe1+εTe0.5Se0.5

Abstract

We present the results of x-ray diffraction, electrical resistivity, and ac magnetic susceptibility measurements on specimens of the “11”-structure superconductor Fe1+εTe0.50Se0.50 (0 ≤ ε ≤ 0.15). Samples were initially either sintered in sealed quartz tubes or melted in a zirconium-gettered arc furnace. Sintered samples were fired two to three times at temperatures of 425°C, 600°C, or 675°C, while arc-melted samples were studied both asmelted and after annealing at 650°C. X-ray diffraction data show a predominant PbO-type tetragonal phase, with a secondary hexagonal NiAs-type phase; for sintered specimens annealed at 600°C, the secondary phase decreases as ε increases over the range 0 ≤ ε ≤ 0.10, with the composition Fe1.10Te0.5Se0.5 exhibiting x-ray phase purity. A higher annealing temperature of 675°C provided such tetragonal phase purity at the composition Fe1.05Te0.5Se0.5. The resistive superconducting transition temperature Tc was nearly independent of the iron concentration 1+ε, suggesting a single superconducting phase, while the magnetic screening fraction varied greatly with concentration and conditions, peaking at ϵ = 0.07, indicating that the amount of superconducting phase is strongly dependent on conditions. We propose that the behaviour can also be viewed in terms of an electron-doped, chalcogen-deficient stoichiometry.