Abstract
SUMMARY A major limitation of the conventional polymer electrolyte membrane fuel cell (PEMFC) catalysts is the fast oxidative degradation of their carbon black supports. Complete replacement of carbon black is difficult because of its low-cost and high electrical conductivity. Reported here are the development and optimization of composite-supported Pt catalysts and the electrosprayed cathode catalyst layer with these catalysts for PEMFC. These catalysts are supported by a composite of carbon black (Vulcan XC-72R) and the electrochemically much more stable carbon-embedded niobium-doped titanium dioxide nanofibers (C/Nb0.1Ti0.9O2). Four different catalyst supports with 20 wt.% Pt were prepared by air spraying and electrospraying to compare their activity and stability. Vulcan XC-72R and C/Nb0.1Ti0.9O2 were tested as pristine support materials for comparison as well as 1:3 and 3:1 mixtures by weight of the two pristine support materials (composite supports). The amount of Nafion in the catalyst ink was optimized for each catalyst layer by a volumetric method. An increase in carbon black content of the support layer from 0% to 100% increases the performance of these catalysts in H2/air PEMFCs but also increases the loss of oxygen reduction reaction mass activity. The best balance between PEMFC performance and durability was obtained for the Pt catalyst with 25% carbon black in the support layer, while the highest initial oxygen reduction reaction mass activity was obtained for the catalyst with 75% carbon black content. Copyright © 2017 John Wiley & Sons, Ltd.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.