Abstract
A great challenge hindering the use of cellulose nanofibers (CNF) as a reinforcing filler in bio-based polymeric matrices are their poor chemical compatibility. This is because of the inherent hydrophilic nature of CNF and the hydrophobic nature of the polymeric matrix. In this study, cellulose laminates were prepared by using CNF as a filler and cellulose acetate butyrate (CAB) as the polymer matrix. To improve the compatibility between CAB and CNF, the residual hydroxyl groups of CAB and the hydroxyl groups on the surface of CNF were cross-linked with bio-derived polyisocyanurate D376N (STABiO™). The composite material was obtained in one step by sandwiching a CNF sheet (10 wt%) coated with a cross-linking agent between CAB films (90 wt%) using hot pressing. When 14.3 wt% of the cross-linking agent to the total weight of CNF and CAB was added, the tensile strength and flexural strength were improved by 72.4% and 16.3%, respectively, compared with neat CAB. It was concluded that this increase in strength is a result of both: cross-linking between the CNF sheets as well as the cross-linking occurring at the CNF/CAB interface.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.